Repair Method for Damaged Porcelain Layer of Glass Lined Equipment

Glass lined equipment is commonly used in industries such as chemical, dyeing, pharmaceutical, and pesticide industries. It is expensive and prone to damage to the ceramic layer if not used properly. Therefore, many engineering and technical personnel at home and abroad have developed many repair techniques for glass lined equipment. The ceramic layer repair of glass lined equipment can be divided into two major categories, namely, body enamel repair and local porcelain blasting repair.

1. Body pond burning repair

Body enamel repair requires overall enamel, commonly known as re enamel. It cannot be repaired on site and can only be enameled in a glass-lined equipment manufacturer. It is mainly applicable to glass lined equipment with large area of porcelain layer damage that cannot be locally repaired on site; "Or the glass lining layer is corroded to a very thin layer, and local repair will be difficult. You can only knock off all the glass layers and re burn the glass layer according to the manufacturing procedure.". The glass lined equipment after pond restoration should be used under reduced pressure or normal pressure according to relevant regulations, depending on the degree of thinning of the container wall thickness.

Repair of partial porcelain explosion of equipment

In the long-term maintenance practice of the glass lining industry, many repair methods have been explored. It is a good thing that expensive glass-lined equipment can be repaired, but failure caused by blind material selection and repair can have extremely adverse consequences for enterprise safety production. Therefore, before repairing glass-lined equipment, it is necessary to fully understand the mechanism of the proposed repair method for glass-lined equipment, and focus on considering whether the equipment repair can bring potential safety hazards.

The repair material should also be tested to simulate the actual production environment to prevent the selected repair material from peeling, cracking, peeling, or even dissolving due to its corrosion resistance.

Therefore, the repair method can be selected based on the specific situation of your equipment. "We have over 25 years of experience in glass lining equipment, and you can trust us with this aspect.".